If a liquid metal alloy is cooled slowly it will eventually form a solid phase. Before it solidifies, however, the liquid undergoes a liquid-liquid transition to a phase in which it has the same concentration but a more strongly ordered structure. This structure has now been demonstrated for the first time by material scientists.